Research Highlights P/Si(111)-6-root-3 surface after a rapid thermal annealing at 950 K. The white protrusions are the newly formed dangling bonds after P desorption. Scale bar: 30 nm. [Surf. Sci. x, xxx (2007)]
P/Si(111)-6-root-3 surface after a rapid thermal annealing at 950 K. The white protrusions are the newly formed dangling bonds after P desorption. Scale bar: 30 nm. [Surf. Sci. x, xxx (2007)]
P/Si(111)-6-root-3 surface after a rapid thermal annealing at 950 K. The white protrusions are the newly formed dangling bonds after P desorption. Scale bar: 30 nm.
[Surf. Sci. x, xxx (2007)]